bluing

英

美

n.  烤蓝; 蓝色漂白剂；上蓝剂; 蓝化；烧蓝；模温过高而引起的绿色氧化膜

化学

COCA.46990

英英释义

noun

• a process that makes something blue (or bluish)
  Synonym:blueing
• used to whiten laundry or hair or give it a bluish tinge
  Synonym:blueingblue

双语例句

• The causes of red exo-frost on bluing coating were analysed, which were higher content of main component in solution, more ferriferous oxide, smaller bluing tank volume, poor operation, repeated workpiece reworking, etc..
  分析了发蓝膜层出现红色挂霜的原因：溶液主要成分含量过高、铁氧化物过多、发蓝槽容量小、工艺操作不当、工件多次返修等。
• Study of Basic Bluing Processing
  关于碱性发兰工艺的分析
• Main Measure For Improving Mechanical Part's Quality of Bluing
  提高机械零件发蓝质量的措施
• BLUING/ BLUE UP: Process of using blue dye to coat a surface of a master, gauge, or piece of product to check a flat, circular, or tapered surface.
  着色检查：使用蓝色染料涂在模具，量规或者产品表面以检查平面、圆面或者锥面的工序。
• Pretreatment, bluing and post treatment of this process were introduced.
  介绍了前处理、发蓝及后处理工序。
• Tapered bores for keyed hubs shall have a minimum of70% transfer of bluing ( surface contact) to the taper gage.
  键槽轮毂的锥孔应至少有70%的着色（表面接触）转移到锥度计上？
• The mechanism and treatment process as well as applying effect of bluing in alkaline media and blackening at room temperature for surface treatment of steel parts were contrasted, the optimal conditions and application using two surface treatment methods in the production were obtained.
  本文作者旨在通过两种表面处理方法的形成机理、工艺流程以及运用效果的对比，得出两种方法在生产上的应用范围和适宜条件。
• By experiment and further application, it has been proved that wastewater from bluing in electroplating plant could be treated by urea reduction, resulting in removal of NO-2 N more than 99.9% and quality of water discharged conforming to our national discharge standard.
  通过对发兰废水处理方法的研究和实践，提出尿素还原法处理发兰废水是可行的，废水中NO-2-N的去除率达99.9%以上，出水水质达到国家排放标准。
• The production shows that the best bluing time in normal temperature is from 4 to 8 minutes and bluing film is bright and anti-corrosion capacity is at or higher than the specified state standard.
  生产实践表明，常温发蓝的最佳发蓝时间为4~8分钟，发蓝膜光亮，耐蚀达到并超过国家规定标准。
• Contrast between Bluing in Alkaline Media and Blackening at Room Temperature for Steel Parts
  钢铁零件热碱发蓝与常温发黑的应用对比